摘要：介紹了醋酸乙烯酯乳液的合成，主要研究引發(fā)劑、乳化劑、反應(yīng)溫度對乳液粘度和固含量的影響。實驗結(jié)果表明，當(dāng)反應(yīng)溫度為75℃，乳化劑、引發(fā)劑用量分別為3mL和2.4mL條件下，得到較高粘度和固含量的乳白色醋酸乙烯酯乳液，乳液粘度為107.5mPa·s、固含量為13.8%、。 關(guān)鍵詞：醋酸乙烯酯乳液；乳化劑；引發(fā)劑；粘度；固含量
Abstract: Introduces the synthesis of vinyl acetate emulsion, the main research cause agent, emulsifier, reaction temperature on the emulsion viscosity and the content of solid influence. The experimental results show that, when the reaction temperature for 75 ℃, emulsifier, dosage of initiator were 3 mL and 2.4 mL condition, we get a higher viscosity and solid content of milky acetate emulsion, emulsion viscosity for 107.5 mPa • s, solid content is 13.8%,. Key words: The vinyl acetate emulsion; Emulsifier; The initiator; Viscosity; Solid content
我國自上世紀(jì)5O年代后期開始聚醋酸乙烯酯乳液的研究工作，1961年在天津市化工研究所實驗廠建成工業(yè)大生產(chǎn)裝置。其后，隨著國內(nèi)十幾個大維尼綸廠的相繼建成投產(chǎn)，到1980年，聚醋酸乙烯酯乳液生產(chǎn)廠家發(fā)展到2O多個，總產(chǎn)量接近10000t[6]。至上世紀(jì)9O年代，我國聚醋酸乙烯酯乳液生產(chǎn)已初具規(guī)模，共有江西維尼綸廠、福建維尼綸廠、貴州有機化工廠、湖南維尼綸廠、山西維尼綸廠等十幾個大維尼綸廠建成投產(chǎn)，總裝置能力達(dá)38．6萬t[7]。 我國聚醋酸乙烯乳液產(chǎn)量約20萬t,消費醋酸乙烯9萬t,占醋酸乙烯總消費量的9.1%。早期的醋酸乙烯酯乳液類產(chǎn)品受合成原料單體及合成工藝路線的限制存在很多缺點，比如放置易沉淀(乳液粒度較大),在使用過程中易結(jié)皮,耐水性差[8]。醋酸乙烯酯類產(chǎn)品從其誕生到現(xiàn)在，價格低一直是其他類成膜劑所不及的。隨著國民經(jīng)濟(jì)的增長，應(yīng)用領(lǐng)域的拓寬，聚醋酸乙烯型乳液膠黏劑的性能、用途已經(jīng)無法滿足市場需求。因此需針對其缺點做進(jìn)一步的改進(jìn)。 本文通過改變引發(fā)劑、乳化劑和反應(yīng)溫度，利用種子乳液聚合方法，對醋酸乙烯酯乳液在不同反應(yīng)條件下的性能進(jìn)行研究。希望能夠為以后的實際應(yīng)用與進(jìn)一步研究提供幫助。 |